性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)ASTM D638/ISO 527380kg/cm²(MPa)[Lb/in2]断裂伸长率ASTM D638/ISO 527200%拉伸模量ASTM D638/ISO 527kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)ASTM D638/ISO 527%拉伸断裂伸长率(延伸率)ASTM D638/ISO 527%弯曲模量(弯曲弹性率)ASTM D790/ISO 17817,000kg/cm²(MPa)[Lb/in2]弯曲强度ASTM D790/ISO 178kg/cm²(MPa)[Lb/in2]洛氏硬度ASTM D785R-105IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 1793kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/inChapy冲击强度23℃ （缺口）ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179kg·cm/cm(J/M)ft·lb/in物性性能比重（密度）ASTM D792/ISO 11830.91成型收缩率ASTM D955%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 113322g/10min220℃/10kgASTM D1238/ISO 1133g/10min吸水率 23℃/24HASTM D570/ISO 62%热性能热变形温度退火ASTM D648/ISO 75120℃（℉）未退火ASTM D648/ISO 75℃（℉）维卡软化点ASTM D1525/ISO R306℃（℉）熔点-℃（℉）燃烧性（率）UL94线性膨胀系数ASTM D696/ISO 11359mm/mm.℃加工条件干燥条件加工温度射嘴℃料筒前段℃料筒中段℃料筒后段℃熔体温度℃模具温度℃压力注塑压力Mpa保压压力Mpa背压Mpa螺杆转速pm其他备注供给部 180 ∼ 200℃，可塑化部 190 ∼ 210℃，计量部 200 ∼ 220℃，成型温度 30 ∼ 50℃，冷却时间 25 ∼ 40sec，注塑压 800 ∼ 1200kg/cm2，保压 600 ∼ 1000kg/cm2颜色高钢性, 长期热稳定特性电器电子生活用品: 电饭煲锅盖 微波炉, 咖啡机、车用复合树脂: 热澌丁 取暖器